Governing Damage Mechanism — Wet H2S Damage (SSC/HIC)
API 571 §4.5.1
Hydrogen-induced cracking (HIC) and sulfide stress cracking (SSC) in carbon/low-alloy steel exposed to wet H2S service. Not detectable by thickness monitoring alone.
Recommended inspection approach: Wet fluorescent magnetic particle (WFMT) and UT shear-wave/AUBT surveys in addition to routine UT thickness, per API RP 571 and NACE SP0296.
This mechanism is crack-dominant — thickness monitoring alone will not detect it. See Standards & Documentation for the full NDE requirement.